PLA Resin 4060d Food Grade for Sealing Agents PLA Fully Biodegradable Material Polylactic Acid

• Customization: Available
• Feature: Biodegradable
• CAS No.: 9051-89-2
• Formula: PLA
• EINECS: PLA
• Material: Polylactic Acid/PLA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film Pressure
• Color: White
• Sample: Available
• MOQ: 1 Kg
• Grade: Extrusion Grade, Blown Film Grade, Injection Moldi
• Application: Optical Grade, Medical Grade, Automotive Parts, Th
• Certificate: TDS COA MSDS
• Transport Package: Bag
• Specification: 25 kg/bag
• Trademark: sysh
• Origin: China
• HS Code: 39077000
• Production Capacity: 500 Tons/Month

Product Description

Product Description

 

   Polylactic Acid(PLA) Granule

 

Polylactic acid (PLA) is a new type of biodegradable material made from starch raw materials proposed from renewable plant resources such as corn. Starch raw materials are fermented to produce lactic acid, which is then converted into polylactic acid through chemical synthesis. It has good biodegradability and can be completely degraded by microorganisms in nature after use, ultimately generating carbon dioxide and water without polluting the environment. This is very beneficial for protecting the environment and is recognized as an environmentally friendly material.

Detailed Photos

 

 

Product Parameters

 

ITEM	UNIT	REFERENCE INDEX
Appearance	-	White or yellow cylindrical granules
Particle Diameter	mm	2~4
Density	g/cm3	1.25±0.05
Monomer	%	≤1
Melt Index(190ºC 2.16kg)	g/10min	1~30
Glass Transition Temperature	ºC	58~60
Melting Point	ºC	~160
Tensile Strength at Break	MPa	~50
Tensile Modulus	GPa	3.5~6.0
Impact Strength	J/m	10~13

Properties	Unit	Test Standard	Data
Density	g/cm3	ASTM D-792	1.22-1.23
Melt Index (210ºC,2.16kg)	g/10min	ASTM D-1238	4.12
Melt Temperature	ºC	DSC	170-190
Vicat Point A/120	ºC	ASTM D-648	55
Tensile Strength	MPa	ASTM D-638	61
Flexural Strength	MPa	ASTM D-790	73
Elongation Break	%	ASTM D-638	22
Water Absorption	%	ASTM D-570	<0.6
Impact Strength	KJ/m2	ASTM D-256	8.8
Printing Temperature	ºC	DSC	200-220

 

Product Usage

PLA downstream is mainly used in textile industry, plastic industry, agricultural plastic film, packaging materials, modern medical materials, 3D printin.

 

Packaging & Shipping

 

25kg/bag, or per your requirement. 25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container

FAQ

1. Are youtrading company or Manufacturer ?

We are factory.

2.About Sample

We provide samples, but you need to pay the sample fee and freight.

3. About Material

We can customize the material according to customers' requirement.

4. About Quality

All the products must be tested strictly according to the testing procedure before shipment.

5. About Delivery Period

Normally delivered in 14 working days after the confirmation of order& payment. And it varies according to the material and quantity.