| Customization: | Available |
|---|---|
| Feature: | Photodegradable |
| Material: | Polyamide(Nylon 6.66)/PA |
|
Still deciding? Get samples of US$ 2/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
PA is short for polyamide, often referred to as Nylon, is a polymer containing repeated amide groups (- NHCO -). PA materials can be made from lactam or from the polycondensation of binary amines and dibasic acids. Nylon was originally developed as a fiber material, such as nylon stockings, but later due to its excellent mechanical properties, such as high strength, rigidity and toughness, as well as good wear resistance and certain chemical stability, PA is also widely used in engineering plastics, in machinery, automobiles, home appliances, aviation and other industrial fields to manufacture various parts, such as gears, bearings and so on. Common PA types include PA6 and PA66.
PA6 Medium viscosit
| Physical property | Standard | Value | Unit |
| Density | ISO 1183 | 1.14 | g/cm³ |
| Shrinkage Flow 30x100x3mm | INTERNAL METHOD | 1.4 | % |
| Shrinkage xFlow 30x100x3mm | INTERNAL METHOD | 1.5 | % |
| Water Absorption 23°C 50RH | INTERNAL METHOD | 3 | % |
| Hardness | Standard | Value | Unit |
| Rockwell Hardness R(Scale) | ISO 2039 | 120 | |
| Rockwell Hardness M(Scale) | ISO 2039 | 80 | |
| Mechanical behavior | Standard | Value | Unit |
| Tensile Modulus | ISO 527 | 2.9 | GPa |
| Tensile Strength Yield | ISO 527 | 80 | MPa |
| Elongation Break | ISO 527 | 30 | % |
| Flexural Strength | ISO 178 | 110 | MPa |
| Flexural Modulus | ISO 178 | 2.7 | GPa |
| Charpy Notch Impact 1eA | ISO 179 | 6 | kJ/m² |
| Physical property | Standard | Value | Unit |
| Density | ISO 1183 | 1.14 | g/cm³ |
| Shrinkage Flow 30x100x3mm | INTERNAL METHOD | 1.2 | % |
| Shrinkage xFlow 30x100x3mm | INTERNAL METHOD | 1.2 | % |
| Water Absorption 23°C 50RH | INTERNAL METHOD | 3.0 | % |
| Hardness | Standard | Value | Unit |
| Rockwell Hardness R(Scale) | ISO 2039 | 120 | |
| Rockwell Hardness M(Scale) | ISO 2039 | 80 | |
| Mechanical behavior | Standard | Value | Unit |
| Tensile Modulus | ISO 527 | 2.8 | GPa |
| Tensile Strength Yield | ISO 527 | 80 | MPa |
| Elongation Break | ISO 527 | 50 | % |
| Flexural Strength | ISO 178 | 110 | MPa |
| Flexural Modulus | ISO 178 | 2.7 | GPa |
| Charpy Notch Impact 1eA | ISO 179 | 8 | kJ/m² |
25kg/bag, or per your requirement. 25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container
Specializing in the production of modified plastics and plastics trade business, our corporation boasts a manufacturing base in the prosperous province of Jiangsu, complemented by strategic warehouse locations in Jiangsu, Hebei, encompassing approximately 8,000 square meters in total area with a seasoned stockpile of approximately 6,000 metric tons at any given time. Our company's primary plastic roster encompasses polypropylene (PP), polyethylene (PE), ethyl vinyl acetate (EVA), polyamide 6 (PA6), polycarbonate (PC), thermoplastic elastomers (TPE), and a vast array of modified plastics, all customizable to suit the unique demands of our clients. These versatile products are adept at making their presence felt in a myriad of industries, such as household appliances, automotive, and electrical equipment.
1. Are youtrading company or Manufacturer ?
We are factory.
2.About Sample
We provide samples, but you need to pay the sample fee and freight.
3. About Material
We can customize the material according to customers' requirement.
4. About Quality
All the products must be tested strictly according to the testing procedure before shipment.
5. About Delivery Period
Normally delivered in 14 working days after the confirmation of order& payment. And it varies according to the material and quantity.