POE is a Polyolefin Elastomer, which is a thermoplastic elastomer derived from the copolymerization of ethylene and high-carbon alpha-olefin (such as octene-1 or decene-1) with a metallocene catalyst. POE has good flexibility, weather resistance and processing properties, while maintaining a certain strength and rigidity. Due to its excellent performance, POE is often used in automotive manufacturing, wire and cable, film products and packaging materials. In addition, in the photovoltaic industry, POE film, as a packaging material, is widely used because of its excellent anti-PID (Potential Induced Degradation, potential induced attenuation) performance, which can improve the efficiency and life of solar panels. When the alpha-olefin content is higher, the material exhibits properties more similar to rubber, which is called POE; When the content is low, it is more manifested as the characteristics of polyethylene (PE).
| Physical property | Standard | Value | Unit |
|---|---|---|---|
| Density | ASTM D792 | 0.902 | g/cm³ |
| Melt Index 190°C 2.16kg | ASTM D1238 | 1.0 | g/10min |
| Mooney Viscosity ML1+4 121°C | ASTM D1646 | 20 | MU |
| Hardness | Standard | Value | Unit |
|---|---|---|---|
| Shore Hardness A 1s Compression Molded | ASTM D2240 | 89 | |
| Shore Hardness D 1s Compression Molded | ASTM D2240 | 42 |
| Mechanical behavior | Standard | Value | Unit |
|---|---|---|---|
| Tensile Modulus 510mm/min Compression Molded 100% Secant | ASTM D638 | 8.00 | MPa |
| Tensile Strength Break 510mm/min Compression Molded | ASTM D638 | 24.8 | MPa |
| Elongation Break 510mm/min Compression Molded | ASTM D638 | 660 | % |
| Tearing Strength Die C | ASTM D624 | 91.2 | KN/m |
| Flexural Modulus 1% Secant Compression Molded | ASTM D790 | 83.1 | MPa |
| Flexural Modulus 2% Secant Compression Molded | ASTM D790 | 81.5 | MPa |
| Thermal | Standard | Value | Unit |
|---|---|---|---|
| Vicat Softening Temperature | ASTM D1525 | 89.0 | °C |
| Melting Temperature DSC 10°C/min | INTERNAL METHOD | 99.0 | °C |
| Glass Transition Temperature | INTERNAL METHOD | -31.0 | °C |
| Crystallization Temperature DSC | INTERNAL METHOD | 84.0 | °C |
POE (polyolefin elastomer) is a thermoplastic elastomer material with good flexibility, weather resistance and processing properties. It is usually used in the following aspects:
1. photovoltaic packaging film: POE film is widely used in the field of solar panel packaging due to its excellent light transmittance and aging resistance.
2. Wire and cable: as an insulating layer or sheath material, suitable for a variety of wire and cable products.
3. Automotive field: Used in the manufacture of automotive seals, shock absorption components.
4. Household items: such as cushions, casters, handles, etc.
5. Shoe materials: Making sports soles, etc.
25kg/bag, or per your requirement. 25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container
1. Are youtrading company or Manufacturer ?
We are factory.
2.About Sample
We provide samples, but you need to pay the sample fee and freight.
3. About Material
We can customize the material according to customers' requirement.
4. About Quality
All the products must be tested strictly according to the testing procedure before shipment.
5. About Delivery Period
Normally delivered in 14 working days after the confirmation of order& payment. And it varies according to the material and quantity.
){kind=link}