STS is an escrow service that protects both buyers and suppliers. Funds are held securely by Made-in-China.com until order terms (e.g., delivery, quality) are fulfilled
|
Still deciding? Get samples of $ !
Request Sample
|
| Customization: | Available |
|---|---|
| Feature: | Biodegradable |
| CAS No.: | 9051-89-2 |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
Payment Guarantee
Platform-protected payments with refund support for eligible order issues.
Platform Logistics
Inspection Service
After-Sales & Dispute Handling
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Polylactic acid (PLA) is a new bio-based and renewable biodegradable material made from starch derived from renewable plant resources such as maize and cassava. Glucose was obtained from starch by saccharification, and then lactic acid with high purity was fermented from glucose and certain strains, and then polylactic acid with certain molecular weight was synthesized by chemical synthesis. It has good biodegradability and can be completely degraded by microorganisms in nature under specific conditions after use, and eventually generate carbon dioxide and water. It does not pollute the environment, which is very beneficial to the protection of the environment and is recognized as environmentally friendly material.
| ITEM | UNIT | REFERENCE INDEX |
| Appearance | - | White or yellow cylindrical granules |
| Particle Diameter | mm | 2~4 |
| Density | g/cm3 | 1.25±0.05 |
| Monomer | % | ≤1 |
| Melt Index(190ºC 2.16kg) | g/10min | 1~30 |
| Glass Transition Temperature | ºC | 58~60 |
| Melting Point | ºC | ~160 |
| Tensile Strength at Break | MPa | ~50 |
| Tensile Modulus | GPa | 3.5~6.0 |
| Impact Strength | J/m | 10~13 |
| Properties | Unit | Test Standard | Data |
| Density | g/cm3 | ASTM D-792 | 1.22-1.23 |
| Melt Index (210ºC,2.16kg) | g/10min | ASTM D-1238 | 4.12 |
| Melt Temperature | ºC | DSC | 170-190 |
| Vicat Point A/120 | ºC | ASTM D-648 | 55 |
| Tensile Strength | MPa | ASTM D-638 | 61 |
| Flexural Strength | MPa | ASTM D-790 | 73 |
| Elongation Break | % | ASTM D-638 | 22 |
| Water Absorption | % | ASTM D-570 | <0.6 |
| Impact Strength | KJ/m2 | ASTM D-256 | 8.8 |
| Printing Temperature | ºC | DSC | 200-220 |
PLA downstream is mainly used in textile industry, plastic industry, agricultural plastic film, packaging materials, modern medical materials, 3D printin.
25kg/bag, or per your requirement. 25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container
1. Are youtrading company or Manufacturer ?
We are factory.
2.About Sample
We provide samples, but you need to pay the sample fee and freight.
3. About Material
We can customize the material according to customers' requirement.
4. About Quality
All the products must be tested strictly according to the testing procedure before shipment.